^{Tape 60 PTFE Film \with Silicone Adhesive 聚四氟乙烯薄膜}

3M Tape 60 has consistent physical and electrical properties over a broad temperature range; for use on
high temperature coils, capacitors and wire harnesses.  2.0-mil PTFE backing.  Silicone thermosetting adhesive. Translucent.

Adhesive: Silicone Thermosetting
Backing: PTFE Film
Backing Thickness: 2.0 Mil
Total Thickness: 4.0 mils/0.102mm
Temperature Class: 180°C /356°F
Dielectric Breakdown: 9500 Volts
Insulation Resistance (megohms): >100000
Breaking Strength: 20 lbs./in. (35 n/10mm)
Elongation (% at break): 200
Electrolytic Corrosion Factor: 1.0
Adhesion to Steel: 30 oz./in. (3.20 n/10mm)
UL Flame Retardant: Yes

Printable: No

厚 2mil 薄膜，在極大溫差時，物理及電氣性能仍保持不變, 適用於高溫線圈,電容器及扁平漆色線。膠黏劑: silicone 微透明  與其相似的#61膠帶，厚5-mil薄膜。 適用于高介電及高斷裂強度的場合  (13"*33M)

^{Tape 61 PTFE Film with Silicone Adhesive 聚四氟乙烯薄膜}

3M Tape 61 has consistent physical and electrical properties over a broad temperature range; for use on
high temperature coils, capacitors and wire harnesses where high dielectric and breaking strength are required. 5.0-mil PTFE backing. Silicone thermosetting adhesive. Translucent.

Adhesive: Silicone Thermosetting
Backing: PTFE Film
Backing Thickness: 5.0 Mil
Total Thickness: 7.0 mils/0.178mm
Temperature Class: 180°C /356°F
Dielectric Breakdown: 15000 Volts
Insulation Resistance (megohms): >100000
Breaking Strength: 45 lbs./in. (79 n/10mm)
Elongation (% at break): 300
Electrolytic Corrosion Factor: 1.0
Adhesion to Steel: 35 oz./in. (3,8 n/10mm)
UL Flame Retardant: Yes

Printable: No

厚 5mil 薄膜，適用於高介電及擊穿強度時使用，在極大溫差時，物理及電氣性能仍保持不變, 適用於高溫線圈 、電容器及扁平漆色線。膠黏劑: silicone 微透明

^{Tape 62 Bondable PTFE Film With Silicone Adhesive 聚四氟乙烯薄膜}

3M PTFE Electrical Tape 62 is supplied on a liner; bondable backside for higher adhesion to its own backing and better bonding of resins and varnishes; for use on high temperature coils, capacitators and wire harnesses. Printable. 2.0-mil PTFE backing, supplied on a liner.  Silicone thermosetting adhesive,• Supplied on 3 inch cores. Translucent.

Adhesive: Silicone Thermosetting
Backing: PTFE Film
Backing Thickness: 2.0 Mil
Total Thickness: 4.0 mils/0.102mm
Temperature Class: 180°C /356°F
Dielectric Breakdown: 9500 Volts
Insulation Resistance (megohms): >100000
Breaking Strength: 20 lbs./in. (35 n/10mm)
Elongation (% at break): 200
Electrolytic Corrosion Factor: 1.0
Adhesion to Steel: 30 oz./in. (3.20 n/10mm)
UL Flame Retardant: Yes

Printable: Yes

厚 2mil 薄膜,有襯紙,具有黏結力強的底部膠黏,能更有效地黏合其帶基,並提高對絕緣漆及樹脂的黏結, 用途與 #60 相似﹔可在表面印刷. 膠黏劑: silicone 微透明

^{Tape 63 PTFE Film With Acrylic Adhesive 聚四氟乙烯薄膜丙烯酸膠黏劑}

3M Tape 63 is for use on coils, capacitors and wire harnesses; solvent-resistant adhesive; for use where
chemical properties are more important than temperature resistance. 2.0-mil PTFE backing,  Acrylic adhesive, Supplied on 3 inch cores. Translucent.

Adhesive: Acrylic
Backing: PTFE Film
Backing Thickness: 2.0 Mil
Total Thickness: 3.5 mils/0.088mm
Temperature Class: 155°C /307°F
Dielectric Breakdown: 9500 Volts
Insulation Resistance (megohms): >100000
Breaking Strength: 20 lbs./in. (35 n/10mm)
Elongation (% at break): 200
Electrolytic Corrosion Factor: 1.0
Adhesion to Steel: 35 oz./in. (3.8 n/10mm)
UL Flame Retardant: Yes

Printable: No

厚 2mil 薄膜,微透明,聚抗溶性的黏結劑,適用於化學性能較耐溫性能重要的情況下.膠黏劑: 丙烯酸. (14"*36YD/支)

^{3M PTFE Pipe Thread Sealant Tape 止洩帶}

Tape 48 is a milky white unfused plastic film made of PTFE fluorocarbon resin. Forms a leak proof seal and helps prevent cross threading on pipe threads.

聚四氟乙烯, Teflon, 特氟龍:耐高溫, 絕緣, 防腐蝕,耐老化,抗微波,自潤滑. 在極大溫差時，物理及電氣性能仍保持不變. 用於螺牙防漏，改善緊密度. 裝置水桶龍頭時，止洩帶可確保不漏. 必須採用相對於螺紋做逆向纏繞，也就是逆時針方向.

^{PTFE Extruded Film Tape 5490  With Silicone Adhesive 鐵氟龍膠帶 助滑}

3M Tape 63 is for use on coils, capacitors and wire harnesses; solvent-resistant adhesive; for use where
chemical properties are more important than temperature resistance. 2.0-mil PTFE backing,  Acrylic adhesive, Supplied on 3 inch cores. Translucent.

Adhesive: Silicone
Backing: PTFE Film
Adhesion to Steel: 27 oz./in. width (29 N/100 mm) D-3330
Tensile Strength: 22 lbs./in. width (385 N/100 mm) D-3759
Elongation at Break: 150% D-3759
Backing Thickness: 2.0 mils (0.05 mm) D-3652
Total Tape Thickness: 3.7 mils (0.09 mm) D-3652
Temperature Use Range: -65° to 400°F (-54° to 204°C)

• Extruded, calendered film tapes that resist curling during unwind and provide an exceptionally smooth surface when applied.
• Extruded PTFE film tapes lie flatter than typical skived PTFE film tapes.
• Thicker backing helps extend the service life, compared to thinner versions, when subjected to abrasion or wear.
• Provides excellent chemical resistance except to organic solvents. Note: The silicone adhesive will be attacked by commercial organic solvents and is not recommended for applications requiring organic resistance.

• Easy-release surface on rollers, plates, belts, etc. where build-up of sticky materials and inks can occur.
• Low coefficient of friction surface on rollers, formers, etc. to facilitate web movement.
• Chemical resistant surface for sealing and masking.
• Wrapping rubber nip rollers on hot polyethylene extrusion machines.

厚 2mil 薄膜,微透明 . (14"*36YD/支)

1. 低摩擦係數 -- 具自然潤滑性質的鐵氟龍面材，可增加許多滾筒材料的操作性。
2. 優異的抗熱性質---耐高熱的鐵氟龍玻璃布膠帶，可提供許多需熱封機器長時間的抗熱性。
3. 抗黏及離形能力 --- 具天然離形效果的鐵氟龍面材，在熱塑件射出時保持滾筒的乾淨，不會形成一層塑膠膜。
4. 抗化學性 --- 鐵氟龍面材提供在嚴苛的設計環境下，具化學阻絕性。
5. 柔軟性 --- 鐵氟龍膠帶在黏貼滾筒時，非常容易使用及有效。
 

3M 鐵氟龍膠帶5490可用於進料階段，藉降低摩擦係數傳送滾輪以幫助印刷片移動更容易。

5491 -  Backing Thickness: 5.0 mils

5491 -  Backing Thickness: 5.0 mils