^{3M Polyimide Film 92 Thermosetting Silicone Adhesive 聚酸亞胺薄膜膠帶矽膠黏劑 92} 無鹵 Non-Halogenated

3M amber Electrical Tape 92 is a 1-mil polyimide film backing with silicone adhesive.
• 1-mil polyimide Kapton backing
• Silicone Adhesive for exceptional heat resistance and may be applied at very low temperatures.
• High temperature applications to 180ºC
• UL510 Flame Retarded

3M Electrical Tape 92 is used for high temperature electrical applications in which a tough, thin insulating material is required for wrapping coils, transformers, capacitors, and wire harnesses. It is also used in printed circuit board assembly as a wave solder masking tape. This tape can be imprinted. On a 3 inch plastic core.

Adhesive: Thermosetting Silicone
Backing: Polyimide film
Backing thickness: 1.0 mil (0.025 mm)
Total thickness: 3.0 mils (0.076 mm)
Insulation Resistance (megohms) >1000000
Dielectric Breakdown: 7,500 Volts
Breaking Strength: 30 lbs/in (53N/10mm)
Elongation(% at break): 55%
Electrolytic Corrosion Factor: 1.0
Adhesion to steel: 25 oz/in (2.8N/10mm)
UL510 Flame Retarded: Yes
Printable: Yes

厚 1mil 薄膜無鹵阻燃膠帶，堅韌 纖薄、特別設計在高溫時使用﹔用於線圈、電容器及電線纏結. 膠黏劑: silicone  操作溫度: 180ºC   30M長 可印字

 #1205 膠帶  厚1-mil薄膜，除具抗溶剂能力外，其他性能与92#相同

^{Polyimide Film 1205 Acrylic Adhesive 聚酸亞胺薄膜膠帶丙烯酸膠黏劑}

3M Polyimide Film Electrical Tape 1205 is used for high-temperature electrical applications in which a tough, thin insulating material that is solvent resistant is required for wrapping coils, transformers, capacitators and wire harnesses.

3M Polyimide Film Electrical Tape 1205 is used as a cover layer material for many types of flexible printed circuits.3M 1205 Tape is used for high-temperature electrical applications in which a tough, thin insulating material that is solvent resistant is required for wrapping coils, transformers, capacitors and wire harnesses. It is also used as a cover layer material for many types of flexible printed circuits.

Adhesive: Acrylic
Backing: Polyimide
Backing Thickness: 1Mil
Total Thickness: 3.0 mils/.076mm
Operating Temperature (continuous): 155°C/311°F
Dielectric Breakdown: 7,500 Volts
Insulation Resistance (megohms):  >1000000
Breaking Strength: 30 lbs./in. (53 n/10mm)
Elongation(% at break): 55
Electrolytic Corrosion Factor: 1.0
Adhesion to Steel: 35 oz./in. (3,8 n/10mm)
UL 510 Flame Retardant: Yes

#1205 無鹵阻燃膠帶    厚 1mil 薄膜，堅韌 纖薄、特別設計在高溫時使用﹔用於線圈、電容器及電線纏結. 具抗溶劑能力  膠黏劑: 丙烯酸膠黏劑  操作溫度: 155ºC，除具抗溶剂能力外，其他性能与92#相同。可印字

^{Polyimide Film 1218 Acrylic Adhesive 聚酸亞胺薄膜膠帶丙烯酸膠黏劑 無鹵 Non-Halogenated}

3M Tape 1218 is a one mil polyimide backing with acrylic adhesive. It is designed for high temperature
applications, in which a solvent resistant backing is required, used on coils, capacitors and wire harnesses. 3M Tape 1218 is available in standard and custom widths and lengths. Standard length is 36 yards.
• 1 mil polyimide backing
• Acrylic adhesive
• Supplied on 3 inch cores

3M Tape 1218 is used for high temperature electrical applications in which a tough, thin insulating material that is solvent-resistant is required for wrapping coils, transformers, capacitors and wire harnesses. It is also used as a cover layer material for many types of flexible printed circuits.

Adhesive:  Acrylic Pressure Sensitive
Backing:  Polyimide
Total thickness:  3.0 mils / 0.076 mm
Operating Temperature: 180°C (356°F)
Adhesion to Steel: 19 oz/in (0.50Kg/in)
Breaking strength: 30 lbs./in (14 Kg/in)
Insulation Resistance: >1000000 megohms
Elongation: (% at break) 55 %
Dielectric Breakdown: 6.0 KV
CTI Group: IIb
Electrolytic Corrosion Factor: 1.0

#1218 無鹵阻燃膠帶  厚 3mil 薄膜，纖薄、特別設計在高溫時使用﹔用於線圈、電容器及電線纏結. 具抗溶劑能力  膠黏劑: 丙烯酸膠黏劑  操作溫度: 180ºC

^{3M Kapton polyimide film 5413 silicone adhesive 聚酸亞胺薄膜膠帶矽膠黏劑 無鹵 Non-Halogenated}

3M Polyimide Film Tape 5413, 2.7 mil (0.07 mm) polyimide film with a silicone adhesive, flame retardant, chemical and radiation resistant

3M Polyimide Film Tape 5413, used as mask for protection of gold fingers of printed circuit boards during wave solder or solder dip process, release surface in fabrication of parts cured at elevated temperatures

Adhesive: silicone
Backing: Kapton Polyimide
Backing Thickness: 2.7Mil
Adhesion to Steel: 22 oz./in. width (24 N/100 mm)

Tensile Strength at Break: 33 lbs./in. width (578 N/100 mm)

Elongation at Break: 62%

Backing Thickness: 1 mil (.03 mm)

Total Tape Thickness: 2.7 mils (.07 mm)

Temperature Use Range: -100°F to +500°F (-73°C to 260°C)

Standard Roll Length: 33m

琥珀色 耐高温 厚 2.7mil 薄膜，特別設計在高溫時電路板防護遮蔽使用.

501mm*36YD (32.9M)

Kapton 是 杜邦 DuPont 的商標  5413 是 3M tape made with DuPont  Kapton

^{3M 5419 Low Static Polyimide Film Tape 3M 5419 低靜電聚酸亞胺薄膜膠帶矽膠黏劑}

3M Low Static Polyimide Film Tape 5419 is a translucent, polyimide film-backed silicone adhesive tape with unique and extremely low electrostatic discharge properties. Conventional polyimide tapes can typically generate over 10,000 volts during use which can damage board mounted electronic components. 3M Low Static Polyimide Film Tape 5419 overcomes this problem without any of the typical drawbacks of conventional “anti-static” or “static-free” tapes (e.g., variable adhesion and opaqueness).

Adhesive: Silicone
Backing: Polyimide

Adhesion to Steel: 20 oz./in. width (22 N/100 mm)
Tensile Strength at Break: 33 lbs./in. width (578 N/100 mm)
Elongation at Break: 60%
Backing Thickness: 1.0 mil (0.03 mm)
Total Tape Thickness: 2.7 mil (0.07 mm)
Temperature Use Range: -100° to 500°F (-73° to 260°C)
Dielectric Strength: 7000 volts D-149
Insulation Resistance: >1000000 ohms
Static Charge: Removal from roll: < 150 volts / Removal from PWB: <50 volts
                    (measured at 50% RH, 70°F (21°C) in an ESD controlled environment)
Outgassing: %TLM = 0.58; %CVCM = 0.24
Flame Retardancy: Pass per UL-510

Standard Roll Length: 33m

琥珀色 耐高温 低靜電   厚 2.7mil 薄膜，特別設計在低靜電電鍍用  防護遮蔽使用.

501mm*36YD (32.9M)

^{3M General Purpose Polyimide Film Tape 7413T  silicone adhesive 聚酸亞胺薄膜膠帶矽膠黏劑}

3M General Purpose Polyimide Film Tape 7413T / 7413TL is a tape consisting of a polyimide film and silicone adhesive designed for solder masking or other very high temperature applications.

Adhesion to Steel: 18 oz./in. width (20 N/100 mm)
Tensile Strength at Break: 29 lbs./in. width (508 N/100 mm)
Elongation at Break: 62%
Backing Thickness: 1.0 mil (0.025 mm)

Total Tape Thickness: 2.4 mils (0.061 mm)
Temperature Use Range: -100°F to 500°F (-73°C to 260°C)

At room temperature, the properties of polyimide and polyester films are similar. However, as the temperature increases, the properties of the polyimide film are less affected than polyester.   Polyimide film does not soften at elevated temperatures, thus the film provides an excellent release surface at elevated temperatures.

Mask for protection of gold fingers of printed circuit boards during wave solder, solder reflow or solder dip process.  Release surface in fabrication of parts cured at elevated temperatures.

琥珀色 耐高温 厚 2.4mil 薄膜，在高溫時使用.  長36YD (32.9M)

^{3M General Purpose Polyimide Film Tape 7418  silicone adhesive 聚酸亞胺薄膜膠帶矽膠黏劑}

3M General Purpose Polyimide Film Tape 7413T / 7413TL is a tape consisting of a polyimide film and silicone adhesive designed for solder masking or other very high temperature applications.

Adhesion to Steel: 20 oz./in. width
Tensile Strength at Break: 20 lbs./in. width
Elongation at Break: 50%
Backing Thickness: 0.025 mm

Total Tape Thickness:  0.063 mm
Temperature Use Range: -50°C to 260°C)

480MM*33M 琥珀色 耐高温

^{3M Polyimide Film 聚酰亞氨薄膜 PIA220 無鹵 Non-Halogenated}

3M Polyimide Film PIA220  is a one mil polyimide backing with acrylic adhesive. It is designed for high temperature applications, in which a solvent resistant backing is required, used on coils, capacitors, transformer and wire harnesses.

 3M Tape PIA220 is available in standard and custom widths and lengths. Standard length is 36 yards.
• 1 mil polyimide backing
• Acrylic adhesive
• Supplied on 3 inch cores

3M Tape PIA220 is used for high temperature electrical applications in which a tough, thin insulating material that is solvent-resistant is required for wrapping coils, transformers, capacitors and wire harnesses. It is also used as a cover layer material for many types of flexible printed circuits.

Adhesive:  Acrylic Pressure Sensitive
Backing:  Polyimide
Total thickness:  2.0 mils / 0.05 mm
Operating Temperature: 220°C (392°F)
Adhesion to Steel: 21oz/in (0.6Kg/in)
Breaking strength: 20 lbs./in (9 Kg/in)
Insulation Resistance: >1000000 megohms
Elongation: (% at break) 35 %
Dielectric Breakdown: 6.0 KV
CTI Group: IIIb
Electrolytic Corrosion Factor: 1.0

PIA220 膠帶 

•厚1mil PET Film  UL510 Flame Retardant
•為無鹵素阻燃膠帶
•堅韌、纖薄，特別設計在高溫時使用，良好抗溶劑能力, 特別設計在高溫時使用﹔用於線圈、電容器及電線纏結. 具抗溶劑能力  膠黏劑: 丙烯酸膠黏劑  操作溫度: 220ºC